产品说明
AMPLIFY TY 2551 Functional Polymer is a maleic anhydride grafted (MAH) polymer. In tie layers for flexible packaging, AMPLIFY TY 2551 Functional Polymer promotes
adhesion of polypropylene to barrier polymers such as polyamide and ethylene vinyl alcohol (EVOH) and other polar substrates.
Main Characteristics:
Excellent adhesion to polyamide, EVOH, polypropylene homopolymers and copolymers
Excellent physical properties
Wide range of service temperature
For blown film, cast film and blow-molded applications
Complies with:
21 CFR 175.105(c)(5)
Consult the regulations for complete details.
基本信息
机构评级FDA 21 CFR 175.105
形式粒子
物理性能额定值单位制测试方法
密度 0.896 g/cm³ ASTM D792
熔流率(熔体流动速率) (230°C/2.16 kg) 5.0 g/10 min ASTM D1238
MAH 接枝水平 1 Low 内部方法
机械性能额定值单位制测试方法
抗张强度 ASTM D638
屈服 23.0 MPa ASTM D638
断裂 17.0 MPa ASTM D638
伸长率 (断裂) 60 % ASTM D638
弯曲模量 - 2% 正割 758 MPa ASTM D790
薄膜额定值单位制测试方法
薄膜厚度 - 经测试 51 μm
膜耐刺穿性 (51 μm) 7.03 J/cm³ 内部方法
割线模量 ASTM D882
2% 正割, MD : 51 μm 758 MPa ASTM D882
2% 正割, TD : 51 μm 703 MPa ASTM D882
抗张强度 ASTM D882
MD : 屈服, 51 μm 27.7 MPa ASTM D882
TD : 屈服, 51 μm 25.0 MPa ASTM D882
MD : 断裂, 51 μm 34.5 MPa ASTM D882
TD : 断裂, 51 μm 22.8 MPa ASTM D882
伸长率 ASTM D882
MD : 断裂, 51 μm 630 % ASTM D882
TD : 断裂, 51 μm 520 % ASTM D882
落锤冲击 (51 μm) 100 g ASTM D1709A
埃尔曼多夫抗撕强度 2 ASTM D1922
MD : 51 μm 20 g ASTM D1922
TD : 51 μm 40 g ASTM D1922
热性能额定值单位制测试方法
维卡软化温度 129 °C ASTM D1525
溶融温度(DSC) 148 °C ASTM D4591
光学性能额定值测试方法
光泽度 (45°, 50.8 μm) 35 ASTM D2457
挤出额定值单位制
熔体温度 221 到 238 °C
挤压说明